Making imprinted particle structure

ABSTRACT

A method of making a multi-layer biocidal structure includes providing a support and locating a first curable layer on the support. A second layer is located on or over the first curable layer, the second layer having multiple biocidal particles located within the second layer. The first curable layer and the second layer are imprinted in a single step with an imprinting stamp having a structure with a depth greater than the thickness of the second layer. The first curable layer is cured to form a first cured layer with a second layer. The imprinting stamp is removed.

CROSS REFERENCE TO RELATED APPLICATIONS

Reference is made to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001857) filed concurrently herewith, entitled Imprinted Multi-layer Structure, by Cok et al, to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001879) filed concurrently herewith, entitled Making Imprinted Multi-layer Structure, by Cok et al, to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001880) filed concurrently herewith, entitled Imprinted Multi-layer Biocidal Particle Structure, by Cok et al, to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001881) filed concurrently herewith, entitled Making Imprinted Multi-layer Biocidal Particle Structure, by Cok et al, to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001882) filed concurrently herewith, entitled Using Imprinted Multi-layer Biocidal Particle Structure, by Cok et al, to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001883) filed concurrently herewith, entitled Imprinted Particle Structure, by Cok et al, to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001885) filed concurrently herewith, entitled Using Imprinted Particle Structure, by Cok et al, and to commonly-assigned U.S. patent application Ser. No. ______ (Attorney Docket No. K001887), entitled Making Colored Biocidal Multi-Layer Structure, by Scheible et al, the disclosures of which are incorporated herein.

FIELD OF THE INVENTION

The present invention relates to biocidal layers having antimicrobial efficacy on a surface.

BACKGROUND OF THE INVENTION

Widespread attention has been focused in recent years on the consequences of bacterial and fungal contamination contracted by contact with common surfaces and objects. Some noteworthy examples include the sometimes fatal outcome from food poisoning due to the presence of particular strains of Escherichia coli in undercooked beef; Salmonella contamination in undercooked and unwashed poultry food products; as well as illnesses and skin irritations due to Staphylococcus aureus and other micro-organisms. Anthrax is an acute infectious disease caused by the spore-forming bacterium bacillus anthracis. Allergic reactions to molds and yeasts are a major concern to many consumers and insurance companies alike. In addition, significant fear has arisen in regard to the development of antibiotic-resistant strains of bacteria, such as methicillin-resistant Staphylococcus aureus (MRSA) and vancomycin-resistant Enterococcus (VRE). The U.S. Centers for Disease Control and Prevention estimates that 10% of patients contract additional diseases during their hospital stay and that the total deaths resulting from these nosocomially-contracted illnesses exceeds those suffered from vehicular traffic accidents and homicides. In response to these concerns, manufacturers have begun incorporating antimicrobial agents into materials used to produce objects for commercial, institutional, residential, and personal use.

Noble metal ions such as silver and gold ions are known for their antimicrobial properties and have been used in medical care for many years to prevent and treat infection. In recent years, this technology has been applied to consumer products to prevent the transmission of infectious disease and to kill harmful bacteria such as Staphylococcus aureus and Salmonella. In common practice, noble metals, metal ions, metal salts, or compounds containing metal ions having antimicrobial properties can be applied to surfaces to impart an antimicrobial property to the surface. If, or when, the surface is inoculated with harmful microbes, the antimicrobial metal ions or metal complexes, if present in effective concentrations, will slow or even prevent altogether the growth of those microbes. Recently, silver sulfate, Ag₂SO₄, described in U.S. Pat. No. 7,579,396, U.S. Patent Application Publication 2008/0242794, U.S. Patent Application Publication 2009/0291147, U.S. Patent Application Publication 2010/0093851, and U.S. Patent Application Publication 2010/0160486 has been shown to provide efficacious antimicrobial protection in polymer composites. The United States Environmental Protection Agency (EPA) evaluated silver sulfate as a biocide and registered its use as part of EPA Reg. No, 59441-8 EPA EST. NO. 59441-NY-001. In granting that registration, the EPA determined that silver sulfate was safe and effective in providing antibacterial and antifungal protection.

Antimicrobial activity is not limited to noble metals but is also observed in other metals such as copper and organic materials such as triclosan, and some polymeric materials.

It is important that the antimicrobial active element, molecule, or compound be present on the surface of the article at a concentration sufficient to inhibit microbial growth. This concentration, for a particular antimicrobial agent and bacterium, is often referred to as the minimum inhibitory concentration (MIC). It is also important that the antimicrobial agent be present on the surface of the article at a concentration significantly below that which can be harmful to the user of the article. This prevents harmful side effects of the article and decreases the risk to the user, while providing the benefit of reducing microbial contamination. There is a problem in that the rate of release of antimicrobial ions from antimicrobial films can be too facile, such that the antimicrobial article can quickly be depleted of antimicrobial active materials and become inert or non-functional. Depletion results from rapid diffusion of the active materials into the biological environment with which they are in contact, for example, water soluble biocides exposed to aqueous or humid environments. It is desirable that the rate of release of the antimicrobial ions or molecules be controlled such that the concentration of antimicrobials remains above the MIC. The concentration should remain there over the duration of use of the antimicrobial article. The desired rate of exchange of the antimicrobial can depend upon a number of factors including the identity of the antimicrobial metal ion, the specific microbe to be targeted, and the intended use and duration of use of the antimicrobial article.

Antimicrobial coatings are known in the prior art, for example as described in U.S. Patent Application Publication No. 2010/0034900. This disclosure teaches a method of coating a substrate with biocide particles dispersed into a coating so that the particles are in contact with the environment. Non-planar coatings are also known to provide surface topographies for non-toxic bio-adhesion control, for example as disclosed in U.S. Pat. No. 7,143,709.

Imprinting methods useful for forming surface topographies are taught in CN102063951. As discussed in CN102063951, a pattern of micro-channels are formed in a substrate using an embossing technique. Embossing methods are generally known in the prior art and typically include coating a curable liquid, such as a polymer, onto a rigid substrate. A pattern of micro-channels is embossed (impressed or imprinted) onto the polymer layer by a master having an inverted pattern of structures formed on its surface. The polymer is then cured.

Fabrics or materials incorporating biocidal elements are known in the art and commercially available. U.S. Pat. No. 5,662,991 describes a biocidal fabric with a pattern of biocidal beads. U.S. Pat. No. 5,980,620 discloses a means of inhibiting bacterial growth on a coated substrate comprising a substantially dry powder coating containing a biocide. U.S. Pat. No. 6,437,021 teaches a water-insoluble polymeric support containing a biocide. Methods for depositing thin silver-comprising films on non-conducting substrates are taught in U.S. Patent Application Publication No. 2014/0170298.

SUMMARY OF THE INVENTION

The efficacy of antimicrobial coatings and materials depend at least in part on their structure and surface area. The cost of the coatings also depends upon the quantity of materials in the coatings. There is a need, therefore, for antimicrobial coatings with improved efficacy and reduced costs.

In accordance with the present invention, a method of making an multi-layer biocidal structure includes:

providing a support;

locating a first curable layer on the support;

locating a second layer on or over the first curable layer, the second layer having multiple biocidal particles located within the second layer;

imprinting the first curable layer and the second layer in a single step with an imprinting stamp having a structure with a depth greater than the thickness of the second layer;

curing the first curable layer to form a first cured layer with a second layer; and

removing the imprinting stamp.

The present invention provides a biocidal multi-layer structure that provides improved antimicrobial properties with thinner layers having increased surface area made in a cost-efficient process.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other features and advantages of the present invention will become more apparent when taken in conjunction with the following description and drawings wherein identical reference numerals have been used to designate identical features that are common to the figures, and wherein:

FIG. 1 is a cross section of a multi-layer structure illustrating an embodiment of the present invention;

FIGS. 2A and 2B are cross sections of multi-layer structures in other embodiments of the present invention;

FIG. 3 is a cross section of a multi-layer structure including particles in an embodiment of the present invention;

FIGS. 4A-4F are cross sections of sequential construction steps useful in a method of the present invention;

FIGS. 5A-5F are cross sections of sequential construction steps useful in another method of the present invention;

FIGS. 6A-6D are cross sections of sequential construction steps useful in yet another method of the present invention;

FIG. 7 is a flow diagram illustrating a method of the present invention;

FIGS. 8A and 8B are flow diagrams illustrating alternative methods of the present invention; and

FIG. 9 is a flow diagram illustrating another method of the present invention.

The Figures are not drawn to scale since the variation in size of various elements in the Figures is too great to permit depiction to scale.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides a multi-layer structure useful in forming an antimicrobial article on a support. Multi-layer structures of the present invention provide improved antimicrobial properties with thinner layers having increased surface area made in a cost-efficient process. In useful methods of the present invention, multiple uncured coatings are formed on a support, imprinted together, and then cured together. A thin top layer can include reduced quantities of antimicrobial materials or antimicrobial particles. The imprinted layers provide a greater surface area for the antimicrobial materials and a topographical structure that inhibits the growth and reproduction of microbes. Coating and imprinting processes provide a cost-efficient manufacturing method.

Referring to FIG. 1, in an embodiment of the present invention, an imprinted multi-layer structure 5 includes a support 30 having a support thickness 36. A bi-layer 7 having a topographical structure is located on or over the support 30. The structured bi-layer 7 includes a first cured layer 10 including a first cross-linked material on or over the support 30 and a second cured layer 20 including a second material different from the first material on or over the first cured layer 10 on a side of the first cured layer 10 opposite the support 30. The first cured layer 10 has a first cured layer thickness 16 and the second cured layer 20 has a second-layer thickness 26. Indentations 80 are located in the first and second cured layers 10, 20 to form a topographical structure with a depth 46. The first material of the first cured layer 10 is cross-linked to the second material of the second cured layer 20 and the depth 46 of the bi-layer 7 structure is greater than the second-layer thickness 26 of the second cured layer 20. Coating or other deposition methods for forming multiple layers on a substrate are known in the art, as are imprinting methods useful for forming the indentations 80 in the first and second cured layers 10, 20.

In an embodiment, the second cured layer 20 is thinner than the first cured layer 10. As shown in FIG. 1, the first cured layer 10 has portions with the first-layer thickness 16 that are thicker than the second-layer thickness 26.

As used herein, a structured layer is a layer that is not smooth or not planar on a microscopic scale corresponding to the magnitude of the indentations 80. For example if the support 30 is planar, a structured layer formed on the support 30 according to the present invention is flat but non-planar and is not smooth. If the support 30 is not planar but is smooth, for example having a surface that is curved in one or more dimensions (such as a spherical section), a structured layer formed on the support 30 according to the present invention is also non-planar but is not smooth. Whether or not the support 30 is planar, the structured layer can include indentations 80, channels, pits, holes, extended portions, mesas or other physical elements or structures. In one embodiment, the surface is rough. The structure depth 46 of the structured bi-layer 7 is the distance from the portion of the structured bi-layer 7 furthest from the support 30 to the portion of the structured bi-layer 7 that is closest to the support 30 in a direction that is orthogonal to a surface of the support 30.

In an embodiment, the first cured layer 10 is located on or over the support 30. The support 30 is any layer that is capable of supporting the first and second cured layers 10, 20 and in different embodiments is rigid, flexible, or transparent and, for example is a substrate made of glass, plastic, paper, or vinyl or combinations of such materials or other materials. In an embodiment, the first cured layer 10 is cross linked to the second cured layer 20 to provide rigidity and improved strength for the layers.

In a useful arrangement, the support 30 is adhered, for example with an adhesive layer 50 such as a pressure-sensitive adhesive or glue such as wall-paper glue, to a surface 8 of a structure 40. The surface 8 is any surface 8, planar or non-planar that is desired to resist the growth of biologically undesirable organisms, including microbes, bacteria, or fungi. In various applications, the structure 40 is a structure such as a wall, floor, table top, door, handle, cover, device, or any structure 40 having the surface 8 likely to come into contact with a human. The imprinted multi-layer structure 5 can form a wall paper or plastic wrap for structures 40.

In an embodiment of the present invention, the second cured layer 20 includes a second material that is different from the first cross-linked material in the first cured layer 10. In another embodiment of the present invention, the second material includes a second cross-linked material that is the same as the first cross-linked material. In this embodiment, either the first cross-linked material includes a third material that is not in the second cross-linked material or the second cross-linked material includes a third material that is not in the first cross-linked material. Therefore, the first cross-linked material and second material are different or include different materials.

In one embodiment, the second cured layer 20 is electrically conductive and the first cured layer 10 is electrically insulating. Electrically conductive materials, for example polyethyldioxythiophene (PEDOT) are known in the art, as are insulating polymers or resins. In an embodiment, the second cured layer 20 is electrically conductive.

Referring to FIG. 2A, in another embodiment the second cured layer 20 (FIG. 1) is chemically patterned to form a patterned second cured layer 21 that has conductive portions 21 a and non-conductive portions 21 b. Materials and methods for pattern-wise inhibiting the electrical conductivity of PEDOT are known. By patterning such inhibiting chemicals over the extent of the second cured layer 20 (FIG. 1), the electrical conductivity of the second cured layer 20 is likewise patterned to form the patterned second cured layer 21 with conductive portions 21 a and non-conductive portions 21 b.

As shown in FIG. 2A in a further embodiment, a binder primer 52 is located between the first cured layer 10 and the support 30. The binder primer 52 can be an adhesive layer 50 that adheres the first cured layer 10 to the support 30. Alternatively, or in addition, the binder primer 52 can form a support surface on which the first cured layer 10 is readily coated, for example by controlling the surface energy of the support surface or the first cured layer 10. In another embodiment not shown in FIG. 1 or 2, the binder primer 52 or the adhesive 50 is located between the first cured layer 10 and the second cured layer 20 or the patterned second cured layer 21 to adhere the first cured layer 10 and the second cured layers 20 or the patterned second cured layer 21 together and enable the second cured layer 20 or the patterned second cured layer 21 to be coated over the first cured layer 10 before the first cured layer 10 and the second cured layer 20 or the patterned second cured layer 21 are imprinted to form the indentations 80 of the bi-layer 7 and the imprinted multi-layer structure 5.

In a useful arrangement illustrated in FIG. 2B, the indentations 80 of the bi-layer 7 contain a third cured material 42, for example electrically conductive material that forms an electrical conductor. In an embodiment, such an electrically conductive third cured material 42 is formed by coating a liquid conductive ink, for example containing metallic nano-particles, over the surface of the structured bi-layer 7, removing the conductive ink from surface portions of the structured bi-layer 7 leaving remaining conductive ink in the indentations 80, and curing the liquid conductive ink to form electrical conductors. Suitable liquid conductive inks are known in the art and are electrically conductive after curing. In another embodiment, the conductivity of the third cured material 42 is greater than the conductivity of the second cured layer 20 or the patterned second cured layer 21.

A combination of the electrically conductive third cured material 42 and the patterned second cured layer 21 with conductive portions 21 a and non-conductive portions 21 b can form an electrical circuit or patterned conductor. The electrical circuit can electrically connect separated electrical conductors in the indentations 80 or can include separate circuits in the indentations 80 and the patterned second cured layer 21. The electrical circuit can connect electronic computing devices such as integrated circuits (not shown).

Referring to FIG. 3 in another useful embodiment of the imprinted multi-layer structure 5 having the bi-layer 7, the second cured layer 20 (FIG. 1) includes particles 60 that can be biocidal particles 60, for example that have a silver component, have a sulfur component, have a copper component, are a salt, are a silver sulfate salt or other biocidal particles, or include phosphors to form a biocidal second cured layer 20 a. In an embodiment, the biocidal second cured layer 20 a has a surface 22 on a side of the biocidal second cured layer 20 a opposite the first cured layer 10 and support 30 and portions of the particles 60 extend beyond the surface 22 forming exposed particles 62. The particles 60 can also have a distribution of sizes so that some of the particles 60 are large particles 64 that can, but do not necessarily, extend beyond the surface 22 and are therefore also exposed particles 62. The particles 60 are located within and between the indentations 80 of the structure bi-layer 7 and include both the large particles 64 and the exposed particles 62.

In this embodiment, the second cured layer 20 (FIG. 1) is a biocidal second cured layer 20 a. By biocidal layer is meant herein any layer that resists the growth of undesirable biological organisms, including microbes, bacteria, or fungi or more generally, eukaryotes, prokaryotes, or viruses. In particular, the biocidal second cured layer 20 a inhibits the growth, reproduction, or life of infectious micro-organisms that cause illness or death in humans or animals and especially antibiotic-resistant strains of bacteria. The biocidal second cured layer 20 a is rendered biocidal by including particles 60 such as ionic metals or metal salts in the biocidal second cured layer 20 a. The particles 60 reside in the biocidal second cured layer 20 a. In an embodiment, some of the particles 60 in the biocidal second cured layer 20 a are exposed particles 62 that extend from the second-layer first side 22 into the environment and can interact with any environmental contaminants or biological organisms in the environment. Exposed particles 62 are thus more likely to be efficacious in destroying microbes. In various embodiments, the particles 60 are silver or copper, are a metal sulfate, have a silver component, are a salt, have a sulfur component, have a copper component, are a silver sulfate salt, or include phosphors. In an embodiment, the biocidal second cured layer 20 a is thinner than the first cured layer 10 so that the second-layer thickness 26 is less than the first-layer thickness 16, thus reducing the quantity of particles 60 that are required in the biocidal second cured layer 20 a. In an alternative embodiment, the second-layer thickness 26 is greater than the first-layer thickness 16.

In an embodiment, the particles 60 are coated, for example with the material in the second cured layer 20 (FIG. 1).

In other embodiments, the biocidal second cured layer 20 a has a thickness that is less than at least one diameter of one or more of the particles 60, has a thickness that is less than a mean diameter of the particles 60, or has a thickness that is less than the median diameter of the particles 60. Alternatively, the particles 60 have at least one diameter between 0.05 and 25 microns. In such embodiments, one or more of the particles 60 will be exposed particles 62. If such exposed particles 62 are biocidal, the exposed particles 62 can inhibit the growth or reproduction of microbes or destroy any microbes on the surface of the biocidal second cured layer 20 a. In yet another arrangement, the biocidal second cured layer 20 a is greater than or equal to 0.5 microns thick and less than or equal to 20 microns thick or the first cured layer 10 on the support 30 includes particles 60 (not shown in FIG. 3).

The indentations 80 form a topographical non-planar layer in the second cured layer 20, the patterned second cured layer 21, or the biocidal second cured layer 20 a that is not smooth and is inhospitable to the growth and reproduction of microbes. In yet another embodiment, the first or second cured layers 10, 20, the patterned second cured layer 21, or the biocidal second cured layer 20 a have a hydrophobic surface, for example by providing a roughened surface either by imprinting or by a treatment such as sandblasting or exposure to energetic gases or plasmas.

Referring to FIGS. 4A to 4F and FIG. 7, a method of the present invention includes making the imprinted multi-layer structure 5 having the support 30 (FIG. 4A) in step 100 (FIG. 7). A first curable layer 13 including a first material is located on or over the support 30 (FIG. 4B) in step 105. A second curable layer 23 including a second material different from the first material is located on or over the first curable layer 13 in step 110 (FIG. 4C) before the first curable layer 13 is cured. The first curable layer 13 and the second curable layer 23 are formed in various ways, including extrusion or coating, for example spin coating, curtain coating, or hopper coating, or other methods known in the art. In other embodiments of the present invention, locating the first curable layer 13 includes laminating a first curable material on or over the support 30 or locating the second curable layer 23 includes laminating a second curable material on or over the first curable layer 13.

The first curable layer 13 and the second curable layer 23 are imprinted in a single step 125 with an imprinting stamp 90 having a structure with a structure depth 46 greater than the second layer thickness 26 of the second curable layer 23 (FIG. 4D) and then cured in a single step 130, for example with heat or radiation 92 to form the first cured layer 10 and the second cured layer 20 (FIG. 4E). The imprinting stamp 90 is removed in step 135 to form an imprinted structured bi-layer 7 with a structure depth 46 greater than the second-layer thickness 26 of the second cured layer 20 (FIG. 4F) to form the structured bi-layer 7 of the imprinted multi-layer structure 5 of the present invention.

An imprinted multi-layer structure 5 having the structured bi-layer 7 of the present invention has been constructed in a method of the present invention using cross-linkable materials such as curable resins (for example using SU8 at suitable viscosities and PEDOT) coated on a glass surface and imprinted using a PDMS stamp to form micro-structures in the bi-layer 7. Electrically conductive PEDOT layers have been patterned to form circuit or wiring patterns and conductive inks have been located and cured in the micro-channels to form cured conductive wires.

Referring further to FIG. 7 in an embodiment of the present invention, the surface 8 of the structure 40 is identified in step 150. The surface 8 is a surface which it is desired to keep free of microbes, for example a wall, floor, table top, door, handle, knob, cover, or device surface, especially any surface 8 found in any type of medical institution. In an embodiment, the surface 8 is planar; in another embodiment, the surface 8 is non-planar. In step 155, an adhesive is located, for example on the surface 8 or on the side of the support 30 opposite the first cured layer 10, to form the adhesive layer 50. The support 30 is adhered to the surface 8 in step 160. In a further embodiment, the support 30, first cured layer 10, and second cured layer 20 are heated to shrink the imprinted multi-layer structure 5 on the surface 8 if the surface 8 is non-planar. In an embodiment, the heating step (not shown separately) is also the adhesion step 160 and a separate adhesive layer 50 is not necessary or used. In an embodiment, the second cured layer 20 is thinner than the first cured layer 10.

In another embodiment, referring to FIG. 2, the third cured material 42, for example a liquid conductive ink, is located in the indentations 80 of the bi-layer 7, for example by coating the surface and indentations 80 of the second cured layer 20 with a liquid conductive ink, wiping the surface of the second cured layer 20 to remove excess liquid conductive ink from the surface but not the indentations 80, and curing the liquid conductive ink in the indentations 80 to form an electrical conductors in each of the indentations 80. Such coating, wiping, and curing methods and materials are known in the art.

Referring next to FIGS. 5A to 5F and to FIG. 7 again, a dispersion of particles 60 is formed in step 120 in the second cross-linkable material for example before locating a biocidal second curable layer 23 a on or over the first curable layer 13 (FIG. 5A). In an embodiment, a dispersion of particles 60 is formed in a carrier such as a liquid, for example a curable resin, in a container 66. Making and coating liquids with dispersed particles is known in the art. A dispersion having antimicrobial particles 60 has been made. The dispersion included three-micron silver sulfate particles milled in an SU8 liquid to an average particle size of one micron, and successfully coated on glass and tested with E. coli bacteria. In an alternative, the biocidal second curable layer 23 a is made separately and laminated on or over the first curable layer 13.

After steps 100 and 105 of FIG. 7 and as shown in FIGS. 4A and 4B, the dispersion is coated or a layer laminated on the first curable layer 13 to form the biocidal second curable layer 23 a (FIG. 5B). The silver sulfate particle dispersion noted above was spin-coated on the glass support 30, cured, and tested for anti-microbial efficacy. As shown in FIG. 5C, the first curable layer 13 and biocidal second curable layer 23 a (the biocidal second curable layer 23 a including the particles 60) on the support 30 are imprinted in step 125 with the stamp 90 and cured with radiation 92 in step 130 to form the first cured layer 10 and biocidal second cured layer 20 a. In an embodiment, the curing step 130 includes cross-linking the first curable layer 13 to the biocidal second curable layer 23 a. The stamp is removed in step 135 to form the imprinted multi-layer structure 5 having the structured bi-layer 7 shown in FIG. 5D. Imprinting methods using stamps are known in the art.

As shown in FIG. 5E, in a further embodiment of the present invention, a portion of the biocidal second cured layer 20 a is removed in step 140, for example by etching or using energetic particles 94 such as with plasma etching, reactive plasma etching, ion etching, or sandblasting the first cured layer 10 or the biocidal second cured layer 20 a. Such a removal treatment can remove any coating over the exposed particles 62 and further expose the exposed particles 62 to the environment. Alternatively, particles 60 are exposed by washing the first or second cured layer 10, 20. In an embodiment, the second-layer thickness 26B after the removal step 140 is less than the second-layer thickness 26A (FIG. 5D) before the removal step 140.

As shown in FIG. 5F, the result of the process is an imprinted multi-layer structure 5 with a structured bi-layer 7 including first cured layer 10 and biocidal second cured layers 20 a on the support 30. The biocidal second cured layer 20 a includes particles 60, including large particles 64 and exposed particles 62 in a second material, for example a second cured material. A coating of silver sulfate particles dispersed in SU8 has been exposed to plasma to reduce the coating thickness and further expose the particles 60 to the environment.

In an embodiment, the first cured layer 10 includes a first cross-linkable material, the biocidal second cured layer 20 a includes a second cross-linkable material and the curing step 130 cross-links the first cross-linkable material to the second cross-linkable material. In another embodiment, the first material includes a first cross-linkable material and the second material includes a second cross-linkable material that is different from the first cross-linkable material and the curing step 130 cross-links the first cross-linkable material to the second cross-linkable material. Alternatively, the first material includes a first cross-linkable material, the second material includes a second cross-linkable material that is the same as the first cross-linkable material, and a third material is included in either the first material or the second material but not both the first and second materials and the curing step 130 cross-links the first cross-linkable material to the second cross-linkable material.

In another embodiment of the present invention, referring back to FIG. 1, the first cured layer 10 and the second cured layer 20 are not necessarily cross-linked. In such an embodiment, the biocidal imprinted multi-layer structure 5 includes the support 30 and the bi-layer 7 having a topographical structure on or over the support 30. The structured bi-layer 7 includes the first cured layer 10 on or over the support 30 and the second cured layer 20 on or over the first cured layer 10 on a side of the first cured layer 10 opposite the support 30. The structure of the structured bi-layer 7 has at least one structure depth 46 that is greater than the second-layer thickness 26 of the second cured layer 20. In an embodiment, multiple biocidal particles 60 are located only in the second cured layer 20.

Similarly, according to a method of the present invention and referring again to FIG. 7 and FIGS. 5A-5F, a method of making a biocidal imprinted multi-layer structure 5 includes providing the support 30 in step 100, locating the first curable layer 13 on the support 30 in step 105, forming a dispersion of multiple biocidal particles 60 in step 120, locating the biocidal second curable layer 23 a on the first curable layer 13 in step 110 using the dispersion, the biocidal second curable layer 23 a having multiple biocidal particles 60 dispersed within the biocidal second curable layer 23 a, imprinting the first curable layer 13 and the biocidal second curable layer 23 a in a single step with an imprinting stamp 90 having a structure with a depth greater than the thickness of the biocidal second curable layer 23 a in step 125, curing the first curable layer 13 and the biocidal second curable layer 23 a in a single step to form the first cured layer 10 and the biocidal second cured layer 20 a in step 130, and removing the imprinting stamp 90 in step 135.

In yet another embodiment of the present invention, not separately illustrated, the layer on a side of the first cured layer 10 opposite the support 30 (e.g. corresponding to the second cured layer 20) is a second layer that is not necessarily a cured layer and is not cross-linked. In various embodiments, this second layer is non-conductive, conductive, pattern-wise conductive, or include biocidal particles 60. The second layer is in a spatial relationship to the first cured layer 10 on a side of the first cured layer 10 opposite the support 30. The structure of the structured bi-layer 7 has at least one structure depth 46 that is greater than the second-layer thickness 26 of the second layer. Multiple biocidal particles 60 are located only in the second layer. In an embodiment the particles 60 are fixed in, fixed on, or adhered to the cross-linked material in the first cured layer 10.

Referring to the sequential structures illustrated in FIGS. 6A-6D and the flow charts of FIGS. 8A and 8B, an alternative method of making a biocidal bi-layer 7 includes providing the support 30 in step 100 and locating the first curable layer 13 on the support 30 in step 105 (as shown in FIG. 7). Referring to FIG. 8A and FIG. 6A, a biocidal second layer 25 a is located on or over the first curable layer 13. The biocidal second layer 25 a includes multiple biocidal particles 60 located within the second cured layer 20.

Referring specifically to FIG. 8A in an embodiment, the biocidal particles 60 are provided in step 300 and then mechanically distributed over the first curable layer 13 in step 305. For example, the particles are agitated within a container or on a surface to form a uniform distribution of particles 60 and then released above the first curable layer 13 so that the particles 60 fall under the influence of gravity onto the first curable layer 13. Ways to distribute particles 60 over a layer are known in the art. The distribution of particles 60 on the first curable layer 13 forms the biocidal second layer 25 a on the first curable layer 13 (equivalent to step 110 in FIG. 7) as shown in FIG. 6A.

Referring specifically to FIG. 8B, in an alternative embodiment, particles 60 are provided in step 300 and dispersed into an evaporable liquid in step 310 (and as shown in step 120 in FIG. 7) to form a dispersion. This dispersion is distinguished from that of FIG. 5A in that is evaporable rather than curable. The dispersion is coated on or over the first curable layer 13 in step 320, for example by spin coating, hopper coating, curtain coating or other methods known in the art. The dispersion is then dried in step 330 (and as shown in step 110 of FIG. 7), for example by heating or drying without curing the first curable layer 13 or at least without completely curing the first curable layer 13, to form the biocidal second layer 25 a. The biocidal second layer 25 a is formed as a layer of particles 60 on the surface of the first curable layer 13 as shown in FIG. 6A.

The first curable layer 13 and the biocidal second layer 25 a are then imprinted with an imprinting stamp having a structure with a depth greater than the thickness of the second curable layer in a single step in step 125, referring now to FIG. 7 and as shown in FIG. 6B. As shown in FIG. 6C, the particles 60 of the biocidal second layer 25 a are impressed by the imprinting stamp into the first curable layer 13. In one embodiment of the present invention, the particles 60 of the biocidal second layer 25 a are impressed completely into the first curable layer 13 so that the biocidal second layer 25 a is a part of the first curable layer 13 (as shown in FIG. 6C) and is transformed into the biocidal second curable layer 23 a. In this case, the biocidal second curable layer 23 a overlaps with the first curable layer 13 so that the entire biocidal second curable layer 23 a is in common with a portion of the first curable layer 13. In an alternative embodiment of the present invention shown in FIG. 6D, at least some of the particles 60 of the biocidal second layer 25 a (FIG. 6B) are impressed only part way into the first curable layer 13 so that the biocidal second curable layer 23 a overlaps a part of the first curable layer 13. The exposed particles 62 extending beyond the surface of the first curable layer 13 (as shown in FIG. 6D) form the biocidal second layer 25 a and does not overlap with the first curable layer 13.

In step 130, the first curable layer 13 and the second curable layer 23 (or biocidal second curable layer 23 a) is cured in a single step to form the first cured layer 10 and second cured layer 20 or biocidal second cured layer 20 a and fix the particles 60 in the bi-layer 7. If the first curable layer 13 includes a cross-linkable material, the step 130 of curing the first curable layer 13 and the second curable layer 23 or biocidal second curable layer 23 a fixes the particles 60 within the cross-linkable material. In step 135, the imprinting stamp is removed. Optionally, a portion of the second layer is removed in step 140 and the bi-layer 7 adhered to the surface 8.

In the embodiments of FIGS. 8A and 8B, the biocidal second curable layer 23 a with the particles 60 is considered to overlap with the first curable layer 13 and the first cured layer 10 so that a portion of the first curable layer 13 is in common with the second curable layer 23 or biocidal second curable layer 23 a. In an alternative understanding, a portion of the first curable layer 13 is converted into the second curable layer 23 or biocidal second curable layer 23 a when the particles 60 are impressed into the first curable layer 13 so that the first curable layer 13 is reduced in thickness and at least a portion of the second curable layer 23 or biocidal second curable layer 23 a is cured. These understandings of the first curable layer 13 and second layer (second curable layer 23, biocidal second curable layer 23 a, or biocidal second layer 25 a) and understanding of the first cured layer 10 and second layer (second cured layer 20, biocidal second cured layer 20 a, biocidal second layer 25 a) are equivalent in practice, since they result in a layer of particles at least partially embedded in the first cured layer 10. Essentially, the second curable layer 23, biocidal second curable layer 23 a, and biocidal second layer 25 a are all embodiments of a second layer formed on first curable layer 13 before the first curable layer 13 is cured to form the first cured layer 10. Likewise, the second cured layer 20, biocidal second cured layer 20 a, and biocidal second layer 25 a are all embodiments of a second layer formed on first cured layer 10 after the first curable layer 13 is cured to form the first cured layer 10. To illustrate these different understandings of the first cured layer 10 and the biocidal second cured layer 20 a or biocidal second layer 25 a, a dashed line demarcates the two layers in FIGS. 6C and 6D. Whether the layers are considered to be separate layers or to overlap is a matter of perspective having little practical consequence.

Thus, in various embodiments, a portion of a second layer is in common with a portion of the first cured layer 10 or an entire second layer is in common with a portion of the first cured layer 10. In various embodiments, the second layer is a curable or cured layer, is non-conductive, is conductive, or includes biocidal particles. In yet another embodiment, cured portions of the second layer are removed (step 140) so that only the particles 60 remain adhered to the first cured layer 10 so that none of the second layer is in common with a portion of the first cured layer 10 (not shown).

In yet another embodiment, the first cured layer 10 or the second cured layer 20, biocidal second cured layer 20 a, or biocidal second layer 25 a have a hydrophobic surface, for example by providing a roughened surface either by imprinting or by a treatment such as sandblasting or exposure to energetic gases or plasmas or from the presence of the biocidal particles 60.

In a further embodiment of the present invention, the first cured layer 10, the second cured layer 20, the biocidal second cured layer 20 a, or the support 30 is or includes a heat-shrink film, for example polyolefin, polyvinylchloride, polyethylene, or polypropylene. Any of the first cured layer 10, the second cured layer 20, the biocidal second cured layer 20 a, or the support 30 can include cross linking materials that are cross linked for example by radiation or heat to provide strength.

Referring to FIG. 9, in various embodiment of the present invention, any of the biocidal bi-layers 7 or the biocidal imprinted multi-layer structures 5 described above, including those of FIG. 3, 5D, 5F, or 6D is located on a surface 8 in step 200 and observed over time in step 205. Periodically or as needed, the imprinted multi-layer structure 5 is cleaned in step 210, for example by washing with water or with a cleaning fluid, or wiping the multi-layer structure 5. The imprinted multi-layer structure 5 is repeatedly observed (step 205) and cleaned (step 210) until it is no longer efficacious for its intended purpose. The biocidal imprinted multi-layer structure 5 is replaced, removed, or covered over in step 220.

In an embodiment, the cleaning step removes dead micro-organisms or dirt from the surface 22 of the biocidal second cured layer 20 a so that the biocidal efficacy of the particles 60 is improved in the absence of the dead micro-organisms or dirt. Useful cleaners include hydrogen peroxide, for example 2% hydrogen peroxide, water, soap in water, or a citrus-based cleaner. In an embodiment, the 2% hydrogen peroxide solution is reactive to make oxygen radicals that improve the efficacy of particles 60. In various embodiments, cleaning is accomplished by spraying the surface 22 of the biocidal second cured layer 20 a with a cleaner and then wiping or rubbing the surface 22. The cleaner can dissolve the biocidal second cured layer 20 a material (e.g. cross linking material) and the wiping or rubbing can remove dissolved material or abrade the surface 22 of the biocidal second cured layer 20 a to expose other particles 60 or increase the exposed surface area of exposed particles 62.

Alternatively, the cleaning or washing step 210 refreshes the particles 60, for example by a chemical process, to improve their biocidal efficacy. This can be done, for example, by ionizing the particles 60, by removing oxidation layers on the particles 60, or by removing extraneous materials such as dust from the particles 60.

Replacement of the biocidal second cured layer 20 a or biocidal second layer 25 a can proceed in a variety of ways. In one embodiment, another biocidal imprinted multi-layer structure 5 is simply located over the biocidal imprinted multi-layer structure 5. Thus, the biocidal multi-layer structure 5 becomes the structure 40 and another biocidal imprinted multi-layer structure 5 is applied to the structure 40, for example with an adhesive layer 50 (FIG. 1). In another embodiment, the biocidal imprinted multi-layer structure 5 is removed and another biocidal imprinted multi-layer structure 5 put in its place. As shown in FIG. 1, the support 30 is adhered to the structure 40 with an adhesive layer 50. Chemical or heat treatments are applied to the biocidal multi-layer structure 5 to loosen, dissolve, or remove the adhesive layer 50 so the biocidal imprinted multi-layer structure 5 can be removed and another adhesive layer 50 applied to the structure 40 to adhere the biocidal imprinted multi-layer structure 5 to the structure 40. In an embodiment, the biocidal imprinted multi-layer structure 5 is peeled from the structure 40 and another biocidal imprinted multi-layer structure 5 having an adhesive layer 50 is adhered to the structure 40.

Alternatively, portions of the biocidal imprinted multi-layer structure 5 are removed, for example at least a portion of the biocidal second cured layer 20 a is mechanically separated from the first cured layer 10. In an embodiment, the biocidal second cured layer 20 a is peeled from the first cured layer 10. Alternatively, the biocidal second cured layer 20 a is abraded and removed by abrasion from the first cured layer 10. In another embodiment, the biocidal second cured layer 20 a is chemically separable from the first cured layer 10 or chemically dissolvable in a substance that does not dissolve the first cured layer 10. In a useful embodiment, a substance that chemically separates the biocidal second cured layer 20 a from the first cured layer 10 or that chemically dissolves the biocidal second cured layer 20 a is a cleaning agent. In an embodiment, the biocidal second cured layer 20 a is repeatedly cleaned, for example by spraying the biocidal second cured layer 20 a with a cleaning agent and then rubbing or wiping the biocidal second cured layer 20 a, and at each cleaning a portion of the biocidal second cured layer 20 a is removed to gradually expose the first cured layer 10.

In another embodiment of the present invention, fluorescent or phosphorescent materials are included in the second cured layer 20 or biocidal second cured layer 20 a and are illuminated. The fluorescent or phosphorescent materials respond to ultra-violet, visible, or infrared illumination and emit light that can be seen or detected and compared to a threshold emission value. Thus, the continuing presence of the second cured layer 20 or biocidal second cured layer 20 a is observed. When light emission in response to illumination is no longer present at a desired level, the second cured layer 20 or biocidal second cured layer 20 a is replaced.

The present invention is useful in a wide variety of environments and on a wide variety of surfaces 8, particularly surfaces 8 that are frequently handled by humans. The present invention can reduce the microbial load in an environment and is especially useful in medical facilities.

The invention has been described in detail with particular reference to certain embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.

PARTS LIST

-   5 multi-layer structure -   7 bi-layer -   8 surface -   10 first cured layer -   13 first curable layer -   16 first-layer thickness -   20 second cured layer -   20 a biocidal second cured layer -   21 patterned second cured layer -   21 a conductive portion -   21 b non-conductive portion -   22 surface -   23 second curable layer -   23 a biocidal second curable layer -   25 a biocidal second layer -   26, 26A, 26B second-layer thickness -   30 support -   36 support thickness -   40 structure -   42 third cured material -   46 structure depth -   50 adhesive layer -   52 binder primer -   60 particle -   62 exposed particle -   64 large particle -   66 container -   80 indentations -   90 stamp -   92 radiation -   94 energetic particles -   100 provide support step -   105 locate first layer step -   110 locate second layer step -   120 form dispersion step -   125 imprint first and second layers step -   130 cure first and second layers step -   135 remove stamp step -   140 remove second layer portion step -   150 identify surface step -   155 locate adhesive step -   160 adhere support to surface step -   200 locate structure step -   205 observe structure step -   210 clean structure step -   220 replace biocidal layer step -   300 provide particles step -   305 mechanically distribute particles on first layer step -   310 disperse particles in evaporable liquid step -   320 coat dispersion on first layer step -   330 evaporate liquid to form second layer step 

1. A method of making a multi-layer biocidal structure, comprising: providing a support; coating a first curable layer on the support; coating a second curable layer including multiple biocidal particles on the first curable layer, the second layer having a thickness within which the multiple biocidal particles are located; imprinting only the first curable layer and the second curable layer in a single step with an imprinting stamp having a structure to form indentations in the first curable layer and the second curable layer having a depth greater than the thickness of the second layer; curing the first curable layer and curing the second curable layer to form a first cured layer and a second cured layer; and removing the imprinting stamp to expose the second cured layer.
 2. The method of claim 1, wherein the step of imprinting includes pressing the particles of the second layer into the first curable layer so that a portion of the first curable layer is in common with the second layer.
 3. The method of claim 2, wherein at least some of the particles of the second layer are impressed only part way into the first curable layer.
 4. The method of claim 2, wherein the particles of the second layer are impressed completely into the first curable layer.
 5. The method of claim 2, further including the step of curing at least a portion of the second layer.
 6. The method of claim 1, further including forming a dispersion including the particles.
 7. The method of claim 6, wherein the step of locating the second layer includes coating the dispersion with the particles on or over the first curable layer.
 8. The method of claim 7, further including processing the dispersion without curing the first curable layer.
 9. The method of claim 8, further including drying the dispersion without curing the first curable layer.
 10. The method of claim 1, wherein the first curable layer includes a cross-linkable material, and the step of curing the first curable layer fixes the particles within the cross-linkable material.
 11. The method of claim 1, wherein locating the first curable layer includes coating or laminating a first curable material on or over the support.
 12. A method of making a multi-layer biocidal structure, comprising: providing a support; providing a first curable layer on the support; providing a second layer on or over the first curable layer, the second layer having multiple biocidal particles located within the second layer; imprinting the first curable layer and the second layer in a single step with an imprinting stamp having a structure with a depth greater than the thickness of the second layer; curing the first curable layer to form a first cured layer; removing the imprinting stamp; and removing a portion of the first cured layer or a portion of the first cured layer and the second layer to expose at least a portion of the surface of at least one of the particles.
 13. The method of claim 12, further including etching, plasma etching, reactive plasma etching, ion etching, or sandblasting the first cured layer or the second layer.
 14. The method of claim 1, wherein the second layer is thinner than a mean or median diameter of the particles.
 15. The method of claim 1, wherein the second layer is thicker than a mean or median diameter of the particles.
 16. The method of claim 1, further including washing the first cured layer or the second layer. 